I use flexfoam IT 3 and a silicon mold to make some LARP-daggers.
The original is very thin, so I hoped the cast daggers would not be too soft, so that they do not bend.
The first dagger I made was surpisingly hard, and did not bend any.
Unfortunately, ever since, the daggers get softer and softer.
Is my batch of flexfoam decaying already? This would be very bad, i did not even use 1 / 10th of it.
Does anyone know other possible causes?
Or even better: a solution?
Can I perhaps change the proportions of the substances to get tougher foam? I do not mind having a bit substance left I cannot use, because at the moment it seems I cannot use any of it.
Thanks in advance!
I use flexfoam IT 3 and a silicon mold to make some LARP-daggers.
The original is very thin, so I hoped the cast daggers would not be too soft, so that they do not bend.
The first dagger I made was surpisingly hard, and did not bend any.
Unfortunately, ever since, the daggers get softer and softer.
Is my batch of flexfoam decaying already? This would be very bad, i did not even use 1 / 10th of it.
Does anyone know other possible causes?
Or even better: a solution?
Can I perhaps change the proportions of the substances to get tougher foam? I do not mind having a bit substance left I cannot use, because at the moment it seems I cannot use any of it.
Thanks in advance!